GP - EAC High - elasticity Acrylic Waterproof Coating

High - elasticity acrylic waterproof coating is a high - elasticity polymer waterproof material. It is an environment - friendly coating scientifically processed from imported self - crosslinking pure acrylic emulsion specially designed for waterproofing as the basic raw material, along with a certain amount of modifiers, activators, additives, pigments and fillers.

Product Features

●It has good overall film - forming properties. After the coating is cured, it forms a continuous, uniform and integrated rubber - like elastic body. Therefore, the waterproof layer made has no overlapping joints, making it more suitable for the construction of special - shaped parts.

●It has good elongation and relatively high tensile strength.

●It is convenient to construct. It can be applied by troweling, spreading or brushing. It has no strict requirements for the substrate temperature and can be applied on wet surfaces. Cold - application construction, especially shows its superiority in construction sites where open flames are prohibited and the shapes are complex.

Application Scope

It is mainly used for waterproofing construction of various roofs, basements, engineering foundations, pools, bathrooms, balconies, etc. Plaster or calcium carbonate powder can be applied on the coated surface, or other decorative materials can be pasted. It is also suitable for the repair of various old roofs.

Precautions

●Construction is not recommended when the temperature is below 5°C.

●Construction is prohibited during rainy or snowy days.

Packaging, Storage and Transportation

●This product is packaged in plastic barrels, with a net weight of 20kg per barrel. The storage temperature should be kept between 5°C and 40°C. Under normal storage conditions, the shelf life is one year.

●This product is non-flammable and non-corrosive, and can be transported as ordinary goods.

Implementation Standard

No.	Test project		Index
			I	Ⅱ
1	tensile strength MPa ≥		1.0	1.5
2	Elongation at break % ≥		300
3	Low - temperature flexibility, bend 180° around a rod with a diameter of 10mm		-10℃ No.cracks	-20℃ No.cracks
4	Water impermeability(0 . 3MPa,30min)		Water - tight
5	Solid content % ≥		65
6	Drying time h	Surface drying time ≤	4
		Hard - drying time ≤	8