GP-FSA Fiber Reinforced Polymer Reactive Adhesive

Fiber-reinforced polymer reactive adhesive is a reactive self-adhesive waterproof membrane suitable for wet-laying construction, which is made of polymer material as the base, double-sided coated with self-adhesive modified asphalt, the lower surface is coated with silicon isolation film or silicon isolation paper, and the upper surface is covered with high-strength polypropylene non-woven fabric as the covering material.

Product Features

●Great adhesive strength and high tear strength
●Non-woven surface friction is great, the product construction can be directly after the decorative decoration (such as paste ceramic tiles, floor tiles, mosaics, smear cement slurry);
●Self-healing, no water leakage, and treats water with softness;
●The material strongly penetrates the base layer, and the hydrophilic molecular chain segments have a high strength and high "bite" with the base layer.

Application Scope

Fiber-reinforced polymer reaction adhesive for non-exposed waterproofing projects. The use of cement mortar or cement mortar bonded to the concrete substrate, the coil should be used between the self-adhesive lap joint.

Constitution method	Main material		Bonding surface	Full thinkness of the coil
Wet-laid	Polymer membrane-based waterproofing membranes	High strength type(H Type)	Single-side adhension(S)	1.5mm,2.0mm
		High extensibility(E类)
Note：other size can be agreed upon by both the supplier and demander

Implementation Standard

Execution standard for physical properties of fiber reinforced polymer reactive adhesive GB/T 35467-2017
No.	Item		Index
			H	E	PY
1	Soluable manner content/(g/m²) ≥		───		2100
2	Tensile property	Tensile force/(N/50mm) ≥	300	200	500
		Elongation at maxmium tensile force/% ≥	50	180	30
		Phenomenon during stetch ≥	NO seperate between the adhensive layer and the polymer membrane or the base fabric
3	Tear force/N ≥		20	25	200
4	Heat resistance(70℃,2h)		No flowing dripping or slipping≤2mm
5	Low tempreture flexibility(-20℃)		No cracks
6	Water impermeability(0.3Mpa,120min)		Water-resistant